| 304 | 304 quality is the basic type of stainless steel. This grade provides high oxidation resistance up to 600-650C.Mechanical resistance and friction resistance are very good | It is preferred in chemical, petrochemical, food, kitchen, automotive industries, all sanitary installation materials, medical industry, boiler and heat exchanger production. Bright, PVC coated, stony and patterned ones are used in all kinds of decoration. |
| 304 L | It’s a low carbon version of TP 304 .It has no friction resistance at temperatures above 500C.It has high oxidation resistance up to 450C. | It is preferred in chemical, mining, petroleum industry and chemical storage tanks.It is generally used at temperatures below 400C. |
| 309 | This grade stainless steel is typical fire resistant up to 850C | Industrial furnace parts, fuel and special pipelines, It is preferred in oil refining. |
| 310 | Oxidation resistance is high at temperatures up to 100C. | It is preferred in industrial furnace parts, fuel and special pipelines, paint industry, oil refining. |
| 316 | It provides high oxidation resistance up to 650C, mechanical rupture and shrinkage strength, as well as high oxidation resistance due to the molybdenum it contains. | Chemical, petro-chemical, food, textile, paper industry, preferred in marine and industrial atmospheric conditions |
| 316 L | It is the low carbon version of TP 316.There is no friction resistance at temperatures above 500C.It has high oxidation resistance up to 450C. | It is preferred in Chemistry, Petro-chemistry, Food, Textile, Paper Industry, marine and industrial atmosphere conditions.It is generally used at temperatures below 400C. |
| 316 TI | General Corrosion resistance is quite similar to TP 316.It has high temperature oxidation resistance up to 650C. | It is preferred in Chemistry, Petro-chemistry, Textile, Paper industry. |
| 310 S | It is very similar to TP 304.Its mechanical and corrosion resistance is slightly better.It can be welded very well and provides very high temperature oxidation resistance up to 1200C. | It is preferred in industrial furnace parts, fuel and special pipelines, paint industry, oil refining. |
| 321 | It provides corrosion resistance between crystals with the addition of TI in its body.This quality has high oxidation resistance at high temperatures up to 900C. The material has very good mechanical and frictional strength. |
Used in resistance and exhaust pipes, manifold, aircraft parts, boiler parts of the chemical industry, printing press knives, salt machines |
| 420 | Does not contain nickel, it can be magnetized. | It is used in making knives. |
| 430 | It provides a good surface appearance, it can be magnetized since it does not contain nickel. | Tableware, interior decoration applications |
| 430 TI | Provides optimum corrosion resistance with the TI addition it contains.Its thermal conductivity is better than TP304. | It is preferred in hot water systems, hot water holding tanks and sugar industry. |
| 409 | It is resistant to high temperature and corrosion. | It is preferred in the production of exhaust pipes. |